engineering resins
LuxCreo's materials science team has developed engineering resins for many industrial and consumer applications. Our materials lead in mechanical properties including resilience, toughness, stiffeness, and flexibility.
EM 01
LUXCREO, INC.
One part elastic material
| Ultimate Tensile Strength, ISO 37 | 8.00 MPa | 1.16 ksi |
| Elongation at Break, ISO 37 | 94 % | 94 % |
| Tear Strength, ASTM D624, Die-C (die cut) | 3.00 kN/m | 17.13 lbf/in |
| Rebound Resilience, ISO 4662 | 34 % | 34 % |
| Tg (DMA, tan(d)), ASTM D4065 | -17.60 ℃ | 0.3 ℉ |
EM+23
LUXCREO, INC.
High elasticity resin
| Hardness, Shore A, ASTM D2240 | 70A | |
| Tear Strength, ASTM D624 Die C 500mm/min | 22.38kN/m | 127.79 lbf/in |
| Tensile modulus, ISO 37 Type Ⅱ 500 mm/min | 5.79 MPa | 0.84 ksi |
| Ultimate Tensile Strength, ISO 37，Type Ⅱ，500 mm/min | 21.59 MPa | 3.13 ksi |
| Elongation at Break, ISO 37，Type Ⅱ，500 mm/min | 560% | 560% |
| Ross Flexing Fatigue (Notched), ASTM D1052 23℃, 90 degree bending, 100 cycles/minute | >250,000 | >250,000 |
| Rebound Resilience, ISO 4662 | 35% | 35% |
LUXCREO, INC.
High elasticity resin
| Hardness, Shore A, ASTM D2240 | 70A | |
| Tear Strength, ASTM D624, Die-C (die cut) | 27.30 kN/m | 155.88 lbf/in |
| Ultimate Tensile Strength, ISO 37 | 16.68 MPa | 2.42 ksi |
| Elongation at Break, ISO 37 | 210% | 210% |
| Ross Flexing Fatigue (Notched), ASTM D1052 23℃, 90 degree bending, 100 cycles/minute | >125,000 | >125,000 |
LUXCREO, INC.
Comparable: ABS
| Tensile Modulus | 1676 Mpa | 243.1 ksi |
| Ultimate Tensile Strength | 48.51 Mpa | 7.04 ksi |
| Hardness, Shore D, ASTM D2240 | 76D | |
| Elongation at Break | 76% | 76% |
| Notched Izod (Machined), 23℃, ISO 180/A | 4.58 kJ/m2 | 2.18 ft-lb/in2 |
| Heat Deflection Temperature @ 0.455 MPa/66 psi, ASTM D648 | 71 ℃ | 160 ℉ |
| Heat Deflection Temperature @ 1.82 MPa/264 psi, ASTM D648 | 48 ℃ | 118 ℉ |
LUXCREO, INC.
Comparable: ABS
| Tensile Modulus, 1 mm/min | 1880 MPa | 272.7 ksi |
| Ultimate Tensile Strength, 10 mm/min | 46.5 MPa | 6.74 ksi |
| Hardness, Shore D, ASTM D2240 | 75D | |
| Elongation at Break, 10 mm/min | 23% | 23% |
| Notched Izod (Machined), 23℃, ISO 180/A | 3.08 kJ/m2 | 1.47 ft-lb/in2 |
| Heat Deflection Temperature @ 0.455 MPa/66 psi, ASTM D648 | 68 ℃ | 154 ℉ |
| Heat Deflection Temperature @ 1.82 MPa/264 psi, ASTM D648 | 47 ℃ | 1116 ℉ |
LUXCREO, INC.
High toughness resin
| Tensile Modulus | 1820 Mpa | 264 ksi |
| Ultimate Tensile Strength | 49.9 Mpa | 7.24 ksi |
| Shore Hardness, ASTM D2240 | 80D | |
| Elongation at Break | 18% | 18% |
| Notched Izod (Machined), 23℃, ISO 180/A | 6.0 KJ/m2 | 2.87 ft-lb/in2 |
| Heat Deflection Temperature @ 0.455 MPa/66 psi | 76.2 ℃ | 169.2 ℉ |
| Heat Deflection Temperature @ 1.82 MPa/264 psi | 60.0 ℃ | 140.0 ℉ |
LUXCREO, INC.
Comparable: ABS
| Flexural Strength | 110 MPa | 16 ksi |
| Flexural Modulus | 4532 MPa | 657.3 ksi |
| Hardness, Shore D, ASTM D2240 | 94D | |
| Heat Deflection Temperature @ 0.455 MPa/66 psi, ASTM D648 | 104.5 ℃ | 220.1 ℉ |
| Heat Deflection Temperature @ 1.82 MPa/264 psi, ASTM D648 | 275 ℃ | 527 ℉ |
LUXCREO, INC.
Water-washable prototyping resin
| Viscosity, 25℃, ASTM D2196 | 180 cps | |
| Flexural Modulus | 1650 MPa | 239.3 ksi |
| Flexural Strength | 57 MPa | 8.3 ksi |
| Hardness, Shore D, ASTM D2240 | 86D |