Mechanical Properties Of TM 79

Flexural Strength

MPa

Flexural Modulus

MPa

Tensile Strength

MPa

Tensile Modulus

MPa

Shore D Hardness

D

Elongation at Break

%
Untitled design (1) copy 2

TM 79 is the material of choice for the application of high toughness and durability parts. TM 79 performance is analogous to PA 12, with excellent low shrinkage and high impact strength. It is an ideal material for rapid prototyping and small batch test parts processing such as wind tunnel testing, electrical enclosures, tooling fixtures and automotive interior and exterior trim. Based on LEAPTM nano- release technology, the components are formed quickly, post-processing is easy, and it has excellent dimensional accuracy and detail resolution.

Tensile Properties, ASTM D638 U.S. U.S. U.S.
Tensile Modulus 243.1 ksi 190.4 ksi 264.0 ksi
Ultimate Tensile Strength 7.04 ksi 5.24 ksi 7.24 ksi
Elongation at Break 76% 95% 18%
Tensile Strength at Yield 6.51 ksi 4.65 ksi 7.61ksi
Elongation at Yield 4.83% 4.58% 5.00%
Impact Properties U.S. U.S. U.S.
Notched Izod (Machined), 23℃, ASTM D256 0.97 ft-lbf/in 1.45 ft-lbf/in 1.68 ft-lb/in
Notched Izod (Machined), -30℃, ASTM D256 0.99 ft-lbf/in 1.10 ft-lbf/in 1.01 ft-lb/in
Notched Izod (Machined), 23℃, ISO 180/A 2.18 ft-lb/in2 2.87 ft-lb/in²
Notched Izod (Machined), -30℃, ISO 180/A 2.06 ft-lb/in2 2.36 ft-lb/in²
Flexural Properties, ASTM D790 U.S. U.S. U.S.
Flexural Strength 9.12 ksi 6.77 ksi 8.76 ksi
Flexural Modulus 236.9 ksi 184.55 ksi 209.7 ksi
Thermal Properties, ASTM D648 U.S. U.S. U.S.
Heat Deflection Temperature @ 0.455 MPa/66 psi,ASTM D648 160 ℉ 158 °F 169.2 ℉
Heat Deflection Temperature @ 1.82 MPa/264 psi, ASTM D648 118 ℉ 140.0 ℉