Dental Materials
LuxCreo enables dental practitioners to print critical dental and orthodontic appliances more efficiently and cost-effectively than traditional manufacturing. LuxCreo leverages cutting-edge innovation in additive manufacturing and expertise in the dental industry to provide a suite of dental resins customized for several orthodontic applications.
- Compatible with Lux 3+ Dental, Lux 3L+, ilux and iLux Pro
- Compatible with LuxFlow, LuxAlign, and LuxLink software
DMR III
LUXCREO, INC.
High accuracy, low shrinkage
| Flexural Modulus | 1948 MPa | 282.46 ksi |
| Flexural Strength | 70 MPa | 10 ksi |
| Hardness Shore D | 88D | |
| Heat Deflection Temperature @ 0.455 MPa/66 psi, ASTM D648 | 55.9 ℃ | 132.6 ℉ |
DMR II
LUXCREO, INC.
High precision, high accuracy
| Tensile Modulus | 2972 MPa | 431.03 ksi |
| Ultimate Tensile Strength | 47 MPa | 6.8 ksi |
| Elongation at Break | 2.07% | 2.07% |
| Notched Izod (Machined) 23_, ASTM D256 | 13.65 J/m | 0.26 ft-lbf/in |
| Heat Deflection Temperature @ 0.455 MPa/66 psi,ASTM D648 | 78.1 Celsius | 172.6 Fahrenheit |
DSG
LUXCREO, INC.
High precision, high-accuracy
| Tensile Modulus | 2950 MPa | 427.8 ksi |
| Ultimate Tensile Strength | 70 MPa | 10.2 ksi |
| Elongation at Break | 4.10% | 4.10% |
| Notched Izod (Machined) 23 Degreees Celcius | 19.4 J/m | 0.364 ft-lbf/in |
| Heat Deflection Temperature @0.455 MPa/66 psi | 81.5 Celsius | 178.7 Fahrenheit |
DNG
LUXCREO, INC.
Tough and biocompatible
| Tensile Modulus | 2127 MPa | 308.5 ksi |
| Ultimate Tensile Strength | 39 MPa | 5.8 ksi |
| Elongation at Break | 14.00% | 14.00% |
| Notched Izod (Machined) 23 Degreees Celcius | 36.7 J/m | 0.69 ft-lbf/in |
| Heat Deflection Temperature @0.455 MPa/66 psi | 71.6 Celsius | 160.8 Fahrenheit |