Mechanical Properties Of TM⁺82
Flexural Strength
Flexural Modulus
Tensile Strength
Tensile Modulus
Shore D Hardness
Elongation at Break
TM+82 is the material of choice for the application of parts with high toughness and impact resistance. TM+82 has the advantages of similar PA 66 material performance, with superior performance such as strong fatigue resistance, strong impact resistance at low temperature and high elongation at break. TM+82 is widely used in the printing of personal wear, medical protective gear, automobiles and industrial parts. Based on LEAPTM nano-release technology, the component molding speed is fast, with excellent dimensional accuracy and detail resolution.
|
|
|
|---|
| Tensile Properties, ASTM D638 | U.S. | U.S. | U.S. |
| Tensile Modulus | 243.1 ksi | 190.4 ksi | 264.0 ksi |
| Ultimate Tensile Strength | 7.04 ksi | 5.24 ksi | 7.24 ksi |
| Elongation at Break | 76% | 95% | 18% |
| Tensile Strength at Yield | 6.51 ksi | 4.65 ksi | 7.61ksi |
| Elongation at Yield | 4.83% | 4.58% | 5.00% |
| Impact Properties | U.S. | U.S. | U.S. |
| Notched Izod (Machined), 23℃, ASTM D256 | 0.97 ft-lbf/in | 1.45 ft-lbf/in | 1.68 ft-lb/in |
| Notched Izod (Machined), -30℃, ASTM D256 | 0.99 ft-lbf/in | 1.10 ft-lbf/in | 1.01 ft-lb/in |
| Notched Izod (Machined), 23℃, ISO 180/A | 2.18 ft-lb/in2 | 2.87 ft-lb/in² | |
| Notched Izod (Machined), -30℃, ISO 180/A | 2.06 ft-lb/in2 | 2.36 ft-lb/in² | |
| Flexural Properties, ASTM D790 | U.S. | U.S. | U.S. |
| Flexural Strength | 9.12 ksi | 6.77 ksi | 8.76 ksi |
| Flexural Modulus | 236.9 ksi | 184.55 ksi | 209.7 ksi |
| Thermal Properties, ASTM D648 | U.S. | U.S. | U.S. |
| Heat Deflection Temperature @ 0.455 MPa/66 psi,ASTM D648 | 160 ℉ | 158 °F | 169.2 ℉ |
| Heat Deflection Temperature @ 1.82 MPa/264 psi, ASTM D648 | 118 ℉ | 140.0 ℉ |